Eco Friendly - LockFloors
Final Product Test Results for heavy metals and other chemicals
PVC – Pass
El PPM\% +/-
Sn 104 27
Fe 84 8
Cr 39 7 Pass
Sr 17.9 1.2
Zn 771 12
Cd ND < 44 Pass
Pb ND < 2.7 Pass
As 4.8 0.4
Ca > 10%
Cl > 10%
Hg 7.1 0.9 Pass
Ti 405 38
Br 4 0.6 Pass
Ba 411 85
RAW MATERIAL PRODUCT DATA SHEET
DESCRIPTION : GP INSULATION AND SHEATHING COMPOUND
APPEARANCE : BLACK PELLETS WHICH GIVE A SMOOTH SURFACE FINISH ONCE EXTRUDED
PROPERTIES UNIT TYPICAL VALUES TEST METHOD
PHYSICAL
RELATIVE DENSITY g/cm3 1.53 SABS METHOD 649
B S S SOFTNESS BSS 20 BS2782 METHOD 365A
SHORE “A” ” A “ 91 CONVERSION TABLE 3
MECHANICAL
(unaged)
TENSILE STRENGTH MPa 13.1 SABS METHOD 503
ELONGATION % 208 SABS METHOD 504
(aged)
(168 hrs @ 100 0C)
TENSILE STRENGTH – RETAINED % 112 SABS METHOD 507
ELONGATION – RETAINED % 91
LOSS OF MASS MAXIMUM mg/cm2 0.3 SABS METHOD 510
OIL IMMERSION
RETENTION OF TENSILE STRENGTH % SABS METHOD 510
RETENTION OF ELONGATION AT BREAK % SABS METHOD 511
RESISTANCE TO PETROLEUM
VARIATION IN VOLUME % SABS METHOD 1017
SIGNS OF STICKING / CRACKS SABS METHOD 150
CHANGE IN COLOUR
LOW TEMPERATURE
COLD BEND 0C -30 SABS METHOD 501
COLD FLEX 0C BS2782 PART 1:METHOD
ELONGATION % BS6469 SEC .,14.992
IMPACT 0C BS6469 SEC .,14.993
HIGH TEMPERATURE
HEAT SHOCK 0C 150 SABS METHOD 500
HEAT DEFORMATION
HOT PRESSURE TEST % 34
ELECTRICAL
VOLUME RESISTIVITY AT 20 0C ohms  cm HEWLETT PACKARD
 
FIRE RETARDANCY
RESISTANCE TO BURNING seconds 6.1 SABS METHOD 502
LIMITING OXYGEN INDEX %
RECOMMENDED PROCESSING TEMPERATURE’S.       (0C)            145/155/165/170